Examples of tests performed

Furnace type	Batch processing technology	Test description
LHS 03/15	Thermocouple heating	Heating to 930 °C, cooling
SV 1001/25 Mk.II	Rotor heating	Heating to 350 °C
PP 140/85	Brake pad heating	Heating to 500 °C, welding test, cooling
PKR 55/95	Soldering brass parts	Flushing with a protective atmosphere, heating to 1050 °C
PKRC 55/95	Annealing of cutting edges	Flushing with a protective atmosphere, heating to 740 °C, cooling to 500 °C, then to 100 °C
PKRC 55/95	Heat treatment of titanium	Flushing with a protective atmosphere, heating to 820 °C, cooling to 200 °C
SV 1001/30 Mk.II	Connector heating	Gradual heating to 135 °C
SV 1001/30 Mk.II	Drying of sand cores	Heating to 100 / 120 °C
PKRC 55/95	Assessment of the degree of surface oxidation of the tool during heat treatment	Heating to 580 °C in a protective atmosphere
SV 1001/30 Mk.II	Heating fats and oils	Heating to 60 °C in a preheated oven
PP 140/85	Determining the appropriate technology for annealing shafts on an industrial scale	Ramp-up to 580 °C, hold at temperature, uncontrolled cooling in a closed furnace
SV 1001/30 Mk.II	Tempering of plastic moldings of automobile headlights to remove internal stress	Preheat the oven to 85 °C, tempering in a preheated oven
PK 105/12	Test of heating of lime-silicate mass in cylinders	Heating to 800 and 1100 °C
SV 1001/30 Mk.II	Verification of the suitability of the furnace for curing transformer paper rolls	Heating to a temperature of 145 °C, holding at temperature